美国杜邦/POM/500P
|
|||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 | |
|
物理性能 |
模收缩 |
|
|
2.2-2.4 |
% |
|
比重 |
|
ASTM D-792 |
1.42 |
| |
|
吸水量 |
浸渍平衡点 |
ASTM D-570 |
0.90 |
% | |
|
吸水量 |
50%相对湿度 |
ASTM D-570 |
0.22 |
% | |
|
吸水量 |
24小时浸渍 |
ASTM D-570 |
0.25 |
% | |
|
机械性能 |
挠曲系数 |
122℃ |
ASTM D-790 |
755 |
MPa |
|
压缩应力 |
23℃,10%变形 |
ASTM D-695 |
123 |
MPa | |
|
IZOD冲击试验 |
23℃ |
ASTM D-256 |
81 |
j/m | |
|
挠曲系数 |
70℃ |
ASTM D-790 |
1720 |
MPa | |
|
挠曲疲劳忍耐限度 |
50%RH,23℃,106周期 |
ASTM D-671 |
31 |
MPa | |
|
洛氏硬度 |
|
ASTM D-785 |
94 |
M scale | |
|
挠曲系数 |
100℃ |
ASTM D-790 |
1030 |
% | |
|
破裂点拉伸变形量 |
70℃ |
ASTM D-638 |
220 |
% | |
|
挠曲系数 |
23℃ |
ASTM D-790 |
3090 |
MPa | |
|
破裂点拉伸变形量 |
-55℃ |
ASTM D-638 |
15 |
% | |
|
压缩应力 |
23℃,1%变形 |
ASTM D-695 |
35 |
MPa | |
|
破裂点拉伸变形量 |
122℃ |
ASTM D-638 |
>260 |
% | |
|
弹性系数 |
23℃ |
ASTM D-638 |
3360 |
MPa | |
|
拉伸强度 |
70℃ |
ASTM D-638 |
48 |
MPa | |
|
洛氏硬度 |
|
ASTM D-785 |
120 |
R scale | |
|
破裂点拉伸变形量 |
23℃ |
ASTM D-638 |
35 |
% | |
|
IZOD冲击试验 |
无缺口23℃ |
ASTM D-256 |
2160 |
j/m | |
|
拉伸强度 |
122℃ |
ASTM D-638 |
26 |
MPa | |
|
拉伸强度 |
-55℃ |
ASTM D-638 |
101 |
MPa | |
|
挠曲变形强度 |
23℃ |
ASTM D-790 |
97 |
MPa | |
|
拉伸强度 |
23℃ |
ASTM D-638 |
69 |
MPa | |
|
IZOD冲击试验 |
缺口-40℃ |
ASTM D-256 |
66 |
j/m | |
|
拉伸强度 |
100℃ |
ASTM D-638 |
36 |
MPa | |
|
抗拉伸冲击强度 |
长试片23℃ |
ASTM D-1822 |
420 |
kj/m2 | |
|
抗剪强度 |
23℃ |
ASTM D-732 |
66 |
MPa | |
|
负载变形量 |
140kg/cm2,50℃ |
ASTM D-621 |
0.5 |
% | |
|
破裂点拉伸变形量 |
100℃ |
ASTM D-638 |
>260 |
% | |
|
挠曲系数 |
-55℃ |
ASTM D-790 |
4530 |
MPa | |
|
电气性能 |
容积电阻率 |
23℃,0.2%含水量 |
ASTM D-257 |
1×1015 |
Ω.cm |
|
抗电弧 |
3.1mm |
ASTM D-495 |
220 |
sec | |
|
介电常数 |
50%RH,23℃,102～106Hz |
ASTM D-150 |
3.7 |
Ω.cm | |
|
介电因数 |
50%RH,23℃,106Hz |
ASTM D-150 |
0.005 |
| |
|
介电强度 |
瞬间Short time(2.3mm) |
ASTM D-149 |
19.7 |
kv/mm | |
|
热性能 |
熔点 |
|
ASTM D-2133 |
175 |
℃ |
|
自燃性 |
|
UL-94 |
HB |
| |
|
线性热膨胀系数 |
-40～29℃ |
ASTM D-696 |
10.4 |
10-5m/m℃ | |
|
热畸变温度 |
0.5MPa |
ASTM D-648 |
172 |
℃ | |
|
热传导系数 |
|
|
0.37 |
W/mk | |
|
线性热膨胀系数 |
60～104℃ |
ASTM D-696 |
13.7 |
10-5m/m℃ | |
|
线性热膨胀系数 |
29～60℃ |
ASTM D-696 |
12.2 |
10-5m/m℃ | |
|
热畸变温度 |
1.8MPa |
ASTM D-648 |
136 |
℃ | |
|
线性热膨胀系数 |
104～160℃ |
ASTM D-696 |
14.9 |
10-5m/m℃ | |
  |